BAUXITE
ROTARY |
GRADE1 |
GRADE2 |
GRADE3 |
Al2O3 |
90%MIN |
88%MIN. |
86%MIN |
Fe2O3 |
1.5%MIN |
1.8%MAX. |
2%MIN |
K2O + Na2O |
0.25%MAX. |
0.25%MAX |
0.25%MAX |
CaO + MgO |
0.5%MAX. |
0.5%MAX |
0.5%MAX |
H2O |
|
1.0%MAX. |
1.0%MAX |
B.D |
3.30G/CCM MIN. |
3.25G/CCM MIN |
3.15G/CCM MIN |
SIZE |
0-25mm |
0-25mm |
0-25mm |
ROUND KILN |
GRADE1 |
GRADE2 |
GRADE3 |
Al2O3 |
90%MIN. |
88%MIN. |
86%MIN. |
Fe2O3 |
1.5%MIN. |
1.8%MAX. |
2%MIN. |
K2O + Na2O |
0.4%MAX. |
0.4%MAX. |
0.4%MAX. |
CaO + MgO |
0.6%MAX. |
0.6%MAX. |
0.6%MAX. |
H2O |
|
1.0%MAX. |
1.0%MAX. |
B.D . |
3.30G/CCM MIN. |
3.25G/CCM MIN. |
3.15G/CCM MIN. |
SIZE |
0-25mm |
0-25mm |
0-25mm |
SHAFT KILN |
GRADE1 |
GRADE2 |
GRADE3 |
Al2O3 |
87%MIN. |
86%MIN. |
85%MIN. |
Fe2O3 |
1.5%MIN. |
2%MAX. |
2%MIN. |
K2O + Na2O |
0.4%MAX. |
0.4%MAX. |
0.4%MAX. |
CaO + MgO |
0.5%MAX. |
0.6%MAX. |
0.6%MAX. |
H2O |
1.0%MAX. |
1.0%MAX. |
1.0%MAX. |
B.D. |
3.15G/CCM MIN. |
3.10G/CCM MIN. |
3.00G/CCM MIN. |
SIZE |
0-25mm |
0-25mm |
0-25mm |
USES: IT IS USED IN REFRACTORY MATERIAL.
PACKING: IN JUMBO BAGS, 20MT/20’FCL
|